PhilaShield 06/07 Heavy Duty 


Two-component, high solids, fast drying and abrasion-resistant coating featuring chemically resistant, polyamine-cured, epoxy mastic technology that can be applied as a primer and finish. It is recommended for high intensity surface treatment, especially for blasting. This product meets the compatibility requirements of various cathode protection systems. Can be used as an all season newbuild and repair coating. Can be used as a single coat, primer, mid coat or finish coat in both air-exposed and immersed environments. Suitable for properly prepared carbon steel substrates. It can be applied at sub-zero surface temperatures. Ideal as a one coat system over marginal or poorly prepared surfaces where blasting is impractical or prohibited. Also meets the criteria for food contact according to FDA section 21, chapter 175.300. Highly recommended choice when surface preparation is upgraded. PhilaShield 06/07 displays very good compatibility with various well known producers.


Applicable on steel structures in aggressive industrial and marine environments especially when a high degree of abrasion resistance is required. Economical for high build applications with long over coating intervals. Can be applied in both above-water and submerged areas including bottoms, topside, deck, superstructure and cargo holds. Can be over-coated with many generic types of paints. Applicable in high film thickness, up to 400 microns. 1. Excellent adhesion to tight rust. 2. Meets USDS Requirements. 3. A high build primer or finish coat. 4. Excellent against “undercutting”. 5. Can be applied up to 12 mils DFT. 6. Easy to apply, self priming on steel. 7. Excellent build to protect sharp edges. 8. Good impact and chemical abrasion resistance. 9. Convenient 4:1 mixing ratio. 10. Excellent salt and fresh water resistance.


Sheen: Semi Glossy

Color: Redbrown, Gray, Aluminum

Solids: 72 ± 2

Coverage: 5.76 m2/Lit at 125 microns dry / 173 microns wet.

Thickness: Over 250 microns dry by 2 coats.

Flashpoint: Mixed product >28°C.

VOC: 255.00g/Lit (material as into the container).

Application Data

Mixing Ratio: Basis 4 part per/volume, Curing Agent 1 part/volume.

Thinner: Not recommended. The material is ready for use, under special conditions use Thinner for Epoxy PH 300, max 5% by volume.

Painting Method: Airless spraying is our recommendation, brush, and spray follows. Tip range 0.48mm-0.66mm (21 thou), blowing pressure shouldn’t be less than 150kg/cm2 (2100psi). May require thinner under special conditions. Use the proper equipment. Safety measures and precautions are very important for the selected method and environment work. Emergency Contact Numbers are available World Wide upon any request.

Cleaning: Power tool cleaning and Cleaners with Universal Thinner.

Readiness Time: 15 minutes in a proper temperature.

Pot Life: 2 hours at 23°C

Curing Time: Within 4 days at 23°C (fully cured).

Drying and Over-Coating Conditions

PhilaShield 0607 Heavy Duty.JPG

Coating Specification

Long overcoat period if temperatures are around freezing point. Proper selection of the systems, coating application procedures and surface preparation are made depending on actual existing film. Best specific design factors and conditions are tested in a controlled laboratory. Consult with Phila Coatings (USA) Inc. Technical Department before and throughout testing process.

Surface Preparation

All surfaces should be clean, dry and free from contamination. High pressure freshwater wash should be conducted prior to the application. Steel products with mill scale: shot blasting or grit blasting should meet the requirements of Sa1 grade in Sweden de-rusting standard at least. Steel products without mill scale: to be ground by dynamic tools to meet the requirements of St3 grade in Sweden de-rusting standard. Steel products painted with plant primer: use slight grit blasting or dynamic tools to carry out secondary surface preparation to meet the requirements of St3 grade in Sweden de-rusting standard. For other surface treatments, please consult with Phila Coatings (USA) Inc.


Circa 18 months at 25°C, stored at dry, shaded and ventilated condition. The container/paint, must be kept sealed and away from heat and ignition sources.

Pack Size

Basis 4 Gal. (16 Lit) pail, agent 1 Gal (3,785 Lit) tin. If other packing specifications are needed, please consult with Phila Coatings (USA) Inc.

Health and Safety

Prior to use, obtain, consult and follow the Material Safety Data Sheet for this product concerning health and safety information. Read carefully and conform to precautions on MSDS and packing vessels. To avoid eye and skin contact, tools such as gloves, goggles and face mask etc. should be used during work with product (proper safety measures should be taken according to construction methods and circumstances). All work with the product must be carried out according to all relevant national health, safety and environment standards and codes. This product is for professional use only.

Limitation of liability

All information is given for guidance only and is subject to regional variation depending upon local climate and environmental condition. An excessive film thickness delays the final curing and creates sagging. Over coating interval will increase with the number of paint layers and the thickness of the paint film. For recommended paints at special circumstances, please consult with our Phila Coatings (USA) Inc. Apply in good weather. The relative humidity must not exceed 80% temperature of the surface to be coated must be at least 3°C above the dew point. All data from the tests is obtained under lab conditions, so Phila Coatings (USA) Inc. won’t bear any liabilities from the condition whether the data could reflect the objective status of the actual application circumstance or not.


The information in the product manual is based on our experiences from tests and practice. For the application without our knowledge, we could only make sure that our products themselves are warranted. We may modify the data in this product manual according to our continuous development and experience accumulation without advanced notice.