VIN/CL Anticorrosive Vinyl Primer


General high build anticorrosive primer, single pack, for seal bottoms, boot tops, topside, cargo holds, on bear steel, shop primers or existing paints. Can be used at low temperatures down to -5 °C. Made from modified vinyl/chlorinated rubber with aluminum. Very good adhesion to various substrates, quick drying. Provides excellent cathodic protection and resistance to sea water. PhilaCoatings VIN/CL Primer can be coated over both chlorinated rubber and upgraded alkyd top coats. As a sealer coat, product is compatible with a broad range of antifouling paints. VIN/CL Anticorrosive Primer displays very good compatibility with various well-known producers.


Complete anticorrosive under water bottom system. Use for repairs and internal and external maintenance. A first class tie coat or sealer for antifouling systems. Compliant with IMO Antifouling System Convention (AFS/CONF/26).


Sheen: Flat

Color: Silver Gray, Oxide Red, Silver Reddish

Solids: 42 ± 2

Coverage: Theoretical Coverage: 5.80 sq. m/Lit at 75 microns dry / 183 microns wet

Thickness: 75 microns dry per coat

Flashpoint: > 28 °C

VOC: 495.0 g/Lit (material as into the container)

Application Data

Mixing Ratio: Single pack product which should be stirred well before application by stirring machine.

Thinner: Not recommended. The material is ready for use, under special conditions use Thinner 400, max 5% by volume.

Painting Method: Airless spraying is our recommendation, brush, and spray follows. Tip range 0.48mm-0.53mm (21 thou), blowing pressure shouldn’t be less than 141kg / cm2 (2000psi). May be required to add thinner. Use proper equipment. Actual safety measures and precautions are very important from the selected method and environment work.

Cleaning: Power tool cleaning with Thinner PH 400.

Drying and Over-Coating Conditions

VINCL Anticorrosive Vinyl Primer.JPG

Coating Specification

At application, environment and design factors can vary significantly, due care should be exercised in the selection, verification of performance and use of the coating. A general guideline of the coating specification is to be maintained for above water uses with the same guidelines as Philacric Modified Acrylic Finish. Under water uses, should always be over coated with selected antifoulings. Please consult Philadelphia Coatings LLC for further information.

Surface Preparation

All surfaces should be clean, dry and free from contamination. High pressure fresh water wash should be applied prior to the treatment of the application. Steel products with mill scale: shot blasting or grit blasting should meet the requirements of Sa1 grade in Sweden derusting standard at least. Steel products without mill scale: to be ground by dynamic tools to meet the requirements of St3 grade in Sweden derusting standard. Steel products painted with plant primer: use slight grit blasting or dynamic tools to carry out secondary surface preparation to meet the requirements of St3 grade in Sweden derusting standard. For other surface treatments, please consult with Philadelphia Coatings LLC.


Circa 24 months at 20 °C, stored at dry, shaded and ventilated condition. The container/paint must be kept sealed and away from heat and ignition.

Pack Size

5 Gal. (18,9 Lit) drum, 20 Lit drum. If other packing specifications are needed, please consult with Philadelphia Coatings LLC.

Health and Safety

Prior to use, obtain, consult and follow the Material Safety Data Sheet for this product concerning health and safety information. Read carefully and conform to precautions on MSDS and packing vessels. To avoid eye and skin contact, tools such as gloves, goggles and face mask etc. should be used during work with product (proper safety measures should be taken according to construction methods and circumstances). All work with the product must be carried out according to all relevant national health, safety and environment standards and codes. This product is for professional use only.

Limitation of liability

All information is given for guidance only and is subject to regional variation depending upon local climate and environmental condition. An excessive film thickness delays the final curing and creates sagging. Over coating interval will increase with the number of paint layers and the thickness of the paint film. For recommended paints at special circumstances, please consult with our Philadelphia Coatings LLC. Apply in good weather. The relative humidity must not exceed 80% temperature of the surface to be coated must be at least 3°C above the dew point. All data from the tests is obtained under lab conditions, so Philadelphia Coatings LLC won’t bear any liabilities from the condition whether the data could reflect the objective status of the actual application circumstance or not.


The information in the product manual is based on our experiences from tests and practice. For the application without our knowledge, we could only make sure that our products themselves are warranted. We may modify the data in this product manual according to our continuous development and experience accumulation without advanced notice.